Pamiętajcie że soldering, brazing, welding....

lutowanie lutowanie twarde spawanie. Są to wspaniałe i niezwykłe procesy łączenia metali !!!

Brazing is a joining process whereby a non-ferrous filler metal or alloy is heated to melting temperature above 450°C (842°F), or, by the traditional definition that has been used in the United States, above 800°F (425)°C and distributed between two or more close-fitting parts by capillary action. At its liquid temperature, the molten filler metal and flux interacts with a thin layer of the base metal, cooling to form an exceptionally strong, sealed joint due to grain structure interaction. With certain metals, such as Nitinol (Nickel Titanium) and Niobium, a low temperature eutectic can form. This leads to the bonding of the two metals at a point that can be substantially lower than their respective melting temperatures. The brazed joint becomes a sandwich of different layers, each metallurgically linked to the adjacent layers. Common brazements are about 1/3 as strong as the materials they join because the metals partially dissolve each other at the interface and usually the grain structure and joint alloy is uncontrolled. To create high-strength brazes, sometimes a brazement can be annealed, or cooled at a controlled rate, so that the joint's grain structure and alloying is controlled. It is also at 1/3 strength because the metal used to braze is usually weaker than the substrate metal because it melts at a lower temperature, ensuring the substrate does not melt.

Soldering is the process in which two metals are joined together by means of a third metal or alloy having a relatively low melting point. Soft soldering is characterized by the value of the melting point of the third metal or alloy, which is below 400°C. The third metal or alloy used in the process is called solder. Soldering is distinguished from brazing by use of a lower melting-temperature filler metal; it is distinguished from welding since the base metal is not melted during the joining process. In a soldering process, heat is applied to the parts to be joined, causing the solder to melt and be drawn into the joint by capillary action and to bond to the materials to be joined by wetting action. After the metal cools, the resulting joints are not as strong as the base metal, but have adequate strength, electrical conductivity, and water-tightness for many uses. Soldering is an ancient technique that has been used practically as long as humans have been making items out of metal.

Welding is a fabrication process that joins materials, usually metals or thermoplastics, by causing coalescence. This is often done by melting the workpieces and adding a filler material to form a pool of molten material (the weld puddle) that cools to become a strong joint, with pressure sometimes used in conjunction with heat, or by itself, to produce the weld. This is in contrast with soldering and brazing, which involve melting a lower-melting-point material between the workpieces to form a bond between them, without melting the workpieces. Arc welding Arc welding Many different energy sources can be used for welding, including a gas flame, an electric arc, a laser, an electron beam, friction, and ultrasound. While often an industrial process, welding can be done in many different environments, including open air, underwater and in space. Regardless of location, however, welding remains dangerous, and precautions must be taken to avoid burns, electric shock, poisonous fumes, and overexposure to ultraviolet light. Until the end of the 19th century, the only welding process was forge welding, which blacksmiths had used for centuries to join metals by heating and pounding them. Arc welding and oxyfuel welding were among the first processes to develop late in the century, and resistance welding followed soon after. Welding technology advanced quickly during the early 20th century as World War I and World War II drove the demand for reliable and inexpensive joining methods. Following the wars, several modern welding techniques were developed, including manual methods like shielded metal arc welding, now one of the most popular welding methods, as well as semi-automatic and automatic processes such as gas metal arc welding, submerged arc welding, flux-cored arc welding and electroslag welding. Developments continued with the invention of laser beam welding and electron beam welding in the latter half of the century. Today, the science continues to advance. Robot welding is becoming more commonplace in industrial settings, and researchers continue to develop new welding methods and gain greater understanding of weld quality and properties.